CYG-DWT(RO) Semi-regid Heat Shrink Dual Wall Tubing

Category: Heat Shrink Busbar Sleeving

Product manual

Material

   Outer layer: irradiation crosslinking modified polyolefin
   Inner layer: modified polyamide hot melt adhesive

Shrink ratio: 4:1

Characteristics

●Semi-hard, flame retarded

●Excellent mechanical, electric and chemical performance;

●Excellent sealing property;

●Continuous use temperature:-40℃~125℃;

● Shrinkage temperature :100℃~150℃

Field of application

This product, designed according to the features of automobile wire harness, is semi-hard and transparent. It has excellent leakproofness, oil resistance and insulativity and conforms to the environmental requirements of RoHS. Meanwhile, it also has excellent mechanical property and thus has come into extensive use in the production of various automobile wire harnesses.

SpecificationDimension before shrinkage(mm)Dimension after full contraction (mm)
Minimum inner diameterMinimum inner diameterTotal wall thickness
5.755.751.251.45±0.30
7.407.401.651.55±0.30
11.011.02.402.35±0.30
14.014.03.002.30±0.30
18.318.34.352.35±0.30
ItemTest MethodIndicator
Radial shrinkage ratioUL224≥50%
Longitudinal length change rateUL224-10%~0
Tensile StrengthASTM D2671≥10.4MPa
Breaking ElongationASTM D2671≥200%
Aging Test Of Hot Air158.0℃±1.0℃/168h-
Tensile Strength After AgingASTM D2671≥7.3MPa
Elongation At Break After AgingASTM D2671≥100%
Cold shock (applicable to outer layer only)ASTM D2671-40℃±2℃,No breakage
Breakdown strengthASTM D2671≥19.7kV/mm
Volume resistivityASTM D876≥1.0x1012Ω· cm
Flame retardantUL22430s,Self-extinguishing
Copper CorrosionUL224158℃,168h,by